The Aurelia Distinct 2922 latex, powder-free, disposable glove has an external surface polymer coating to help prevent tapes and adhesives from sticking to the glove, and an internal polymer coating, reducing surface friction and allowing it to be put on more easily than uncoated, powder-free gloves, particularly in wet environments. The glove has a palm thickness of 5 mils and a finger thickness of 6 mils, and is 9.4" long from the tip of the middle finger to the edge of the beaded wrist cuff, which is 2 mils thick. Latex provides better elasticity than nitrile, chloroprene, or vinyl, and better puncture resistance than vinyl. The glove has a honeycomb texture for better grip than regular textured gloves. This ambidextrous white glove is suitable for dental and medical examination applications.
Specifications
| Material | Latex, powder free |
| Palm thickness | 5 mils |
| Finger thickness | 6 mils |
| Cuff thickness | 2 mils |
| Length | 9.4" |
| Color | White |
| Minimum tensile strength | 30.0 to 31.3 megapascals (MPa) before aging and 27.3 to 28.0 MPa after aging |
| Elongation before aging | 960 to 970% |
| Elongation after aging | 890 to 920% |
| Acceptable Quality Level (AQL) | 1.5 |
Tensile strength, measured in MPa, is the amount of force required to rip a glove; the higher the number, the stronger the glove material. Elongation measures how much a glove can be stretched before it breaks. It is expressed as a percent of the original length of the glove at the moment of breakage; the higher the percent, the more the glove can stretch. AQL is an FDA quality specification for the de